详细介绍
AWS A5.17 F6A0-EL12 F7A2-EM12K
GB/T5293 F4A0-H08A F5A2-H08MnA
DIN BAR 188AC10KM
Discription and applications:
Acid agglomerated flux for welding of ordinary carbon, low alloy structure and boiler quality steel matching with suitable SAW wire(such as EL8, EM12, EM12K). The flux suitable for high speed welding and provides very good weld bead appearance and excellent slag detachability even with narrow groove and fillet welds. The other character of HFX-SJ501 is high anti-cracking and anti-blowhole ability. Especially it is insensitive to oil, rust, scale and dirt on the surface to be welded. Most being used to double-side with single pass weld and fillet welds. As the consumption of the flux is very low, It it very economical.
Flux type: Aluminium titanium
Basicity index: 0.5-0.8
Grain size: 2.0-0.28mm(10-60 meshes)
Weight: 25kg/bag
Export Markets: Gloal
Compositions of fluxes (%)：
|
SiO2+TiO2 |
MnO+AI2O3 |
CaF2 |
S |
P |
|
25-35 |
50-60 |
3-10 |
≤0.06 |
≤0.08 |
Typical mechanical properties of deposited metal：
|
Wire matched |
Yield Strength Ó s (MPa) |
Tensile Strength Ó b (MPa) |
Elongation δ 5% |
AKV (J) |
|
|
20°C |
0°C |
||||
|
H08A |
≥330 |
415-550 |
≥22 |
≥50 |
≥27 |
|
H08MnA |
≥400 |
480-650 |
≥22 |
≥50 |
≥27 |
|
EL12 |
≥330 |
415-550 |
≥22 |
- |
≥27 |
|
EM12K |
≥400 |
480-650 |
≥22 |
- |
≥27 |
NOTICE:
1. Before welding, fluxes should be baked for 2 hours at 300-350°C.
2. Removal of rust, oil, water and impurities etc. in welding area.